Luminescence of phosphorus containing oxide materials: Crystalline SiO2‐P and 3P2O5⋅7SiO2; CaO⋅P2O5; SrO⋅P2O5 glasses
2014
Luminescence of phosphate glasses such as CaO⋅P2O5 and SrO⋅P2O5 is compared with that of phosphorus doped crystalline α-quartz and phosphosilicate glass with content 3P2O5⋅7SiO2. Water & OH groups are found by IR spectra in these materials. The spectrum of luminescence contains many bands in the range 1.5 - 5.5 eV. The luminescence bands in UV range at 4.5-5 eV are similar in those materials. Decay duration in exponential approximation manifests a time constant about 37 ns. Also a component in μs range was detected. PL band of μs component is shifted to low energy with respect to that of ∼37 ns component. This shift is about 0.6 eV. It is explained as singlet-triplet splitting of excited st…
UV and yellow luminescence in phosphorus doped crystalline and glassy silicon dioxide
2015
Abstract Luminescence of phosphorus doped crystalline α-quartz and phosphosilicate glass with content 3P2O5·7SiO2 was studied. Water and OH groups are found by IR spectra in these materials. The spectrum of luminescence contains many bands in the range 1.5–5.5 eV. The luminescence bands in UV range at 4.5–5 eV are similar in those materials. Decay duration in exponential approximation manifests a time constant about 37 ns. Also a component in µs range was detected. PL band of µs component is shifted to low energy with respect to that of ~37 ns component. This shift is about 0.6 eV. It is explained as singlet–triplet splitting of excited state. Below 14 K increase of luminescence kinetics du…